Solder Alloy 124 vs. AWS E410NiMo

Solder alloy 124 belongs to the otherwise unclassified metals classification, while AWS E410NiMo belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is solder alloy 124 and the bottom bar is AWS E410NiMo.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 17
190
Elongation at Break, % 46
17
Poisson's Ratio 0.44
0.28
Shear Modulus, GPa 5.8
76
Tensile Strength: Ultimate (UTS), MPa 27
850

Thermal Properties

Latent Heat of Fusion, J/g 24
280
Melting Completion (Liquidus), °C 330
1440
Melting Onset (Solidus), °C 320
1400
Specific Heat Capacity, J/kg-K 130
480
Thermal Conductivity, W/m-K 22
24
Thermal Expansion, µm/m-K 29
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.6
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 7.7
3.1

Otherwise Unclassified Properties

Base Metal Price, % relative 70
10
Density, g/cm3 11
7.8
Embodied Carbon, kg CO2/kg material 4.1
2.4
Embodied Energy, MJ/kg 68
34
Embodied Water, L/kg 470
110

Common Calculations

Stiffness to Weight: Axial, points 0.83
14
Stiffness to Weight: Bending, points 7.6
25
Strength to Weight: Axial, points 0.65
30
Strength to Weight: Bending, points 1.8
26
Thermal Diffusivity, mm2/s 15
6.5
Thermal Shock Resistance, points 3.9
23

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.12
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.060
Chromium (Cr), % 0
11 to 12.5
Copper (Cu), % 0 to 0.080
0 to 0.75
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
79 to 84.6
Lead (Pb), % 97.2 to 98.2
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
0.4 to 0.7
Nickel (Ni), % 0 to 0.010
4.0 to 5.0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 0.9
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 1.8 to 2.2
0
Zinc (Zn), % 0 to 0.0010
0