Solder Alloy 124 vs. Grade 200 Maraging Steel
Solder alloy 124 belongs to the otherwise unclassified metals classification, while grade 200 maraging steel belongs to the iron alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is solder alloy 124 and the bottom bar is grade 200 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 17 | |
| 190 |
| Elongation at Break, % | 46 | |
| 9.1 to 18 |
| Poisson's Ratio | 0.44 | |
| 0.3 |
| Shear Modulus, GPa | 5.8 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 27 | |
| 970 to 1500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 24 | |
| 260 |
| Melting Completion (Liquidus), °C | 330 | |
| 1460 |
| Melting Onset (Solidus), °C | 320 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 460 |
| Thermal Expansion, µm/m-K | 29 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 70 | |
| 31 |
| Density, g/cm3 | 11 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 4.5 |
| Embodied Energy, MJ/kg | 68 | |
| 59 |
| Embodied Water, L/kg | 470 | |
| 140 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.83 | |
| 13 |
| Stiffness to Weight: Bending, points | 7.6 | |
| 23 |
| Strength to Weight: Axial, points | 0.65 | |
| 33 to 51 |
| Strength to Weight: Bending, points | 1.8 | |
| 27 to 35 |
| Thermal Shock Resistance, points | 3.9 | |
| 29 to 45 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0.050 to 0.15 |
| Antimony (Sb), % | 0 to 0.12 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Cobalt (Co), % | 0 | |
| 8.0 to 9.0 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 67.8 to 71.8 |
| Lead (Pb), % | 97.2 to 98.2 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 3.5 |
| Nickel (Ni), % | 0 to 0.010 | |
| 17 to 19 |
| Phosphorus (P), % | 0 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 | |
| 0 to 0.1 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.010 |
| Tin (Sn), % | 1.8 to 2.2 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.15 to 0.25 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |