Solder Alloy 132 vs. AWS BAu-5
Both solder alloy 132 and AWS BAu-5 are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 15 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is solder alloy 132 and the bottom bar is AWS BAu-5.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 37 | |
| 140 |
| Poisson's Ratio | 0.39 | |
| 0.37 |
| Shear Modulus, GPa | 13 | |
| 50 |
| Tensile Strength: Ultimate (UTS), MPa | 52 | |
| 210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 45 | |
| 180 |
| Melting Completion (Liquidus), °C | 190 | |
| 1170 |
| Melting Onset (Solidus), °C | 180 | |
| 1140 |
| Specific Heat Capacity, J/kg-K | 180 | |
| 280 |
| Thermal Expansion, µm/m-K | 25 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 13 |
Common Calculations
| Stiffness to Weight: Axial, points | 2.3 | |
| 5.8 |
| Stiffness to Weight: Bending, points | 12 | |
| 13 |
| Strength to Weight: Axial, points | 1.6 | |
| 4.5 |
| Strength to Weight: Bending, points | 3.5 | |
| 6.0 |
| Thermal Shock Resistance, points | 4.1 | |
| 9.0 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0.2 to 0.5 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 29.5 to 30.5 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 |
| Lead (Pb), % | 38.5 to 40.3 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 35.5 to 36.4 |
| Palladium (Pd), % | 0 | |
| 33.5 to 34.5 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 59.5 to 60.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |