Solder Alloy 134 vs. AWS E310

Solder alloy 134 belongs to the otherwise unclassified metals classification, while AWS E310 belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is solder alloy 134 and the bottom bar is AWS E310.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 31
200
Elongation at Break, % 31
34
Poisson's Ratio 0.4
0.27
Shear Modulus, GPa 11
79
Tensile Strength: Ultimate (UTS), MPa 38
620

Thermal Properties

Latent Heat of Fusion, J/g 41
300
Melting Completion (Liquidus), °C 230
1400
Melting Onset (Solidus), °C 190
1360
Specific Heat Capacity, J/kg-K 170
480
Thermal Conductivity, W/m-K 45
14
Thermal Expansion, µm/m-K 26
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 9.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 100
26
Density, g/cm3 9.6
7.9
Embodied Carbon, kg CO2/kg material 8.5
4.6
Embodied Energy, MJ/kg 140
65
Embodied Water, L/kg 820
200

Common Calculations

Stiffness to Weight: Axial, points 1.8
14
Stiffness to Weight: Bending, points 11
25
Strength to Weight: Axial, points 1.1
22
Strength to Weight: Bending, points 2.6
20
Thermal Diffusivity, mm2/s 28
3.7
Thermal Shock Resistance, points 3.4
15

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 2.0 to 2.4
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.25
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.080 to 0.2
Chromium (Cr), % 0
25 to 28
Copper (Cu), % 0 to 0.080
0 to 0.75
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
44.5 to 53.9
Lead (Pb), % 56.5 to 58.5
0
Manganese (Mn), % 0
1.0 to 2.5
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0 to 0.010
20 to 22.5
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
0 to 0.75
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 39.5 to 40.5
0
Zinc (Zn), % 0 to 0.0010
0