Solder Alloy 134 vs. N06985 Nickel

Solder alloy 134 belongs to the otherwise unclassified metals classification, while N06985 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is solder alloy 134 and the bottom bar is N06985 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 31
210
Elongation at Break, % 31
45
Poisson's Ratio 0.4
0.28
Shear Modulus, GPa 11
80
Tensile Strength: Ultimate (UTS), MPa 38
690

Thermal Properties

Latent Heat of Fusion, J/g 41
320
Melting Completion (Liquidus), °C 230
1350
Melting Onset (Solidus), °C 190
1260
Specific Heat Capacity, J/kg-K 170
450
Thermal Conductivity, W/m-K 45
10
Thermal Expansion, µm/m-K 26
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 10
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 9.6
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 100
55
Density, g/cm3 9.6
8.4
Embodied Carbon, kg CO2/kg material 8.5
8.8
Embodied Energy, MJ/kg 140
120
Embodied Water, L/kg 820
270

Common Calculations

Stiffness to Weight: Axial, points 1.8
14
Stiffness to Weight: Bending, points 11
23
Strength to Weight: Axial, points 1.1
23
Strength to Weight: Bending, points 2.6
21
Thermal Diffusivity, mm2/s 28
2.6
Thermal Shock Resistance, points 3.4
16

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 2.0 to 2.4
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.25
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
21 to 23.5
Cobalt (Co), % 0
0 to 5.0
Copper (Cu), % 0 to 0.080
1.5 to 2.5
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
18 to 21
Lead (Pb), % 56.5 to 58.5
0
Manganese (Mn), % 0
0 to 1.0
Molybdenum (Mo), % 0
6.0 to 8.0
Nickel (Ni), % 0 to 0.010
35.9 to 53.5
Niobium (Nb), % 0
0 to 0.5
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0
0 to 1.0
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.030
Tin (Sn), % 39.5 to 40.5
0
Tungsten (W), % 0
0 to 1.5
Zinc (Zn), % 0 to 0.0010
0