Solder Alloy 136 vs. Nickel 600

Solder alloy 136 belongs to the otherwise unclassified metals classification, while nickel 600 belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is solder alloy 136 and the bottom bar is nickel 600.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 25
190
Elongation at Break, % 19
3.4 to 35
Poisson's Ratio 0.42
0.29
Shear Modulus, GPa 8.9
75
Tensile Strength: Ultimate (UTS), MPa 34
650 to 990

Thermal Properties

Latent Heat of Fusion, J/g 34
310
Melting Completion (Liquidus), °C 260
1410
Melting Onset (Solidus), °C 190
1350
Specific Heat Capacity, J/kg-K 150
460
Thermal Conductivity, W/m-K 40
14
Thermal Expansion, µm/m-K 27
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 9.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
1.8

Otherwise Unclassified Properties

Base Metal Price, % relative 90
55
Density, g/cm3 10
8.5
Embodied Carbon, kg CO2/kg material 6.8
9.0
Embodied Energy, MJ/kg 110
130
Embodied Water, L/kg 680
250

Common Calculations

Stiffness to Weight: Axial, points 1.4
13
Stiffness to Weight: Bending, points 9.5
23
Strength to Weight: Axial, points 0.92
21 to 32
Strength to Weight: Bending, points 2.3
20 to 26
Thermal Diffusivity, mm2/s 26
3.6
Thermal Shock Resistance, points 3.6
19 to 29

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0.5 to 2.0
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.25
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
14 to 17
Copper (Cu), % 0 to 0.080
0 to 0.5
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
6.0 to 10
Lead (Pb), % 71.9 to 75
0
Manganese (Mn), % 0
0 to 1.0
Nickel (Ni), % 0 to 0.010
72 to 80
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.015
Tin (Sn), % 24.5 to 25.5
0
Zinc (Zn), % 0 to 0.0010
0