Solder Alloy 136 vs. R60901 Alloy

Both solder alloy 136 and R60901 alloy are otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is solder alloy 136 and the bottom bar is R60901 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 25
98
Elongation at Break, % 19
17 to 22
Poisson's Ratio 0.42
0.34
Shear Modulus, GPa 8.9
37
Tensile Strength: Ultimate (UTS), MPa 34
500 to 580

Thermal Properties

Latent Heat of Fusion, J/g 34
250
Specific Heat Capacity, J/kg-K 150
270
Thermal Conductivity, W/m-K 40
17
Thermal Expansion, µm/m-K 27
6.3

Otherwise Unclassified Properties

Density, g/cm3 10
6.6
Embodied Water, L/kg 680
270

Common Calculations

Stiffness to Weight: Axial, points 1.4
8.3
Stiffness to Weight: Bending, points 9.5
23
Strength to Weight: Axial, points 0.92
21 to 25
Strength to Weight: Bending, points 2.3
21 to 24
Thermal Diffusivity, mm2/s 26
9.7
Thermal Shock Resistance, points 3.6
58 to 67

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0.5 to 2.0
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.25
0
Cadmium (Cd), % 0 to 0.0050
0
Copper (Cu), % 0 to 0.080
0
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
0
Lead (Pb), % 71.9 to 75
0
Nickel (Ni), % 0 to 0.010
0
Niobium (Nb), % 0
2.4 to 2.8
Silver (Ag), % 0 to 0.1
0
Tin (Sn), % 24.5 to 25.5
0
Zinc (Zn), % 0 to 0.0010
0
Zirconium (Zr), % 0
96.8 to 97.5
Residuals, % 0
0 to 0.29