Solder Alloy 137 vs. C55283 Copper
Solder alloy 137 belongs to the otherwise unclassified metals classification, while C55283 copper belongs to the copper alloys. There are 17 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is solder alloy 137 and the bottom bar is C55283 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 24 | |
| 100 |
| Poisson's Ratio | 0.42 | |
| 0.34 |
| Shear Modulus, GPa | 8.3 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 34 | |
| 190 |
Thermal Properties
| Latent Heat of Fusion, J/g | 33 | |
| 190 |
| Melting Completion (Liquidus), °C | 270 | |
| 720 |
| Melting Onset (Solidus), °C | 190 | |
| 640 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 400 |
| Thermal Expansion, µm/m-K | 27 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 6.3 | |
| 7.9 |
| Embodied Energy, MJ/kg | 100 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.3 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 9.2 | |
| 18 |
| Strength to Weight: Axial, points | 0.9 | |
| 6.1 |
| Strength to Weight: Bending, points | 2.2 | |
| 8.5 |
| Thermal Shock Resistance, points | 3.7 | |
| 8.0 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0.5 to 3.0 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Copper (Cu), % | 0 to 0.080 | |
| 86.2 to 87.2 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 |
| Lead (Pb), % | 75.9 to 80 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 7.0 to 7.5 |
| Silver (Ag), % | 0 to 0.1 | |
| 5.8 to 6.2 |
| Tin (Sn), % | 19.5 to 20.5 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.15 |