Solder Alloy 137 vs. N06603 Nickel

Solder alloy 137 belongs to the otherwise unclassified metals classification, while N06603 nickel belongs to the nickel alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is solder alloy 137 and the bottom bar is N06603 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 24
190
Elongation at Break, % 19
28
Poisson's Ratio 0.42
0.28
Shear Modulus, GPa 8.3
76
Tensile Strength: Ultimate (UTS), MPa 34
740

Thermal Properties

Latent Heat of Fusion, J/g 33
320
Melting Completion (Liquidus), °C 270
1340
Melting Onset (Solidus), °C 190
1300
Specific Heat Capacity, J/kg-K 150
480
Thermal Conductivity, W/m-K 38
11
Thermal Expansion, µm/m-K 27
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 8.9
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 7.7
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 85
50
Density, g/cm3 10
8.2
Embodied Carbon, kg CO2/kg material 6.3
8.4
Embodied Energy, MJ/kg 100
120
Embodied Water, L/kg 660
300

Common Calculations

Stiffness to Weight: Axial, points 1.3
13
Stiffness to Weight: Bending, points 9.2
24
Strength to Weight: Axial, points 0.9
25
Strength to Weight: Bending, points 2.2
22
Thermal Diffusivity, mm2/s 25
2.9
Thermal Shock Resistance, points 3.7
20

Alloy Composition

Aluminum (Al), % 0 to 0.0010
2.4 to 3.0
Antimony (Sb), % 0.5 to 3.0
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.25
0
Cadmium (Cd), % 0 to 0.0050
0
Carbon (C), % 0
0.2 to 0.4
Chromium (Cr), % 0
24 to 26
Copper (Cu), % 0 to 0.080
0 to 0.5
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
8.0 to 11
Lead (Pb), % 75.9 to 80
0
Manganese (Mn), % 0
0 to 0.15
Nickel (Ni), % 0 to 0.010
57.7 to 65.6
Phosphorus (P), % 0
0 to 0.2
Silicon (Si), % 0
0 to 0.5
Silver (Ag), % 0 to 0.1
0
Sulfur (S), % 0
0 to 0.010
Tin (Sn), % 19.5 to 20.5
0
Titanium (Ti), % 0
0.010 to 0.25
Yttrium (Y), % 0
0.010 to 0.15
Zinc (Zn), % 0 to 0.0010
0.010 to 0.1