Solder Alloy 137 vs. R30012 Cobalt
Solder alloy 137 belongs to the otherwise unclassified metals classification, while R30012 cobalt belongs to the cobalt alloys. There are 23 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is solder alloy 137 and the bottom bar is R30012 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 24 | |
| 220 |
| Elongation at Break, % | 19 | |
| 1.0 |
| Poisson's Ratio | 0.42 | |
| 0.28 |
| Shear Modulus, GPa | 8.3 | |
| 86 |
| Tensile Strength: Ultimate (UTS), MPa | 34 | |
| 830 |
Thermal Properties
| Latent Heat of Fusion, J/g | 33 | |
| 320 |
| Melting Completion (Liquidus), °C | 270 | |
| 1470 |
| Melting Onset (Solidus), °C | 190 | |
| 1280 |
| Specific Heat Capacity, J/kg-K | 150 | |
| 440 |
| Thermal Conductivity, W/m-K | 38 | |
| 15 |
| Thermal Expansion, µm/m-K | 27 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.9 | |
| 1.8 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.7 | |
| 1.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 10 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 6.3 | |
| 8.3 |
| Embodied Energy, MJ/kg | 100 | |
| 120 |
| Embodied Water, L/kg | 660 | |
| 480 |
Common Calculations
| Stiffness to Weight: Axial, points | 1.3 | |
| 14 |
| Stiffness to Weight: Bending, points | 9.2 | |
| 23 |
| Strength to Weight: Axial, points | 0.9 | |
| 26 |
| Strength to Weight: Bending, points | 2.2 | |
| 22 |
| Thermal Diffusivity, mm2/s | 25 | |
| 3.8 |
| Thermal Shock Resistance, points | 3.7 | |
| 23 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0.5 to 3.0 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.25 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0050 | |
| 0 |
| Carbon (C), % | 0 | |
| 1.4 to 2.0 |
| Chromium (Cr), % | 0 | |
| 27 to 32 |
| Cobalt (Co), % | 0 | |
| 47.5 to 64.1 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 3.0 |
| Lead (Pb), % | 75.9 to 80 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 1.0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 3.0 |
| Silicon (Si), % | 0 | |
| 0 to 2.0 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 19.5 to 20.5 | |
| 0 |
| Tungsten (W), % | 0 | |
| 7.5 to 9.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |