Solder Alloy 151 vs. Grade 1 Babbitt Metal
Both solder alloy 151 and grade 1 Babbitt Metal are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. They have 50% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is solder alloy 151 and the bottom bar is grade 1 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 39 | |
| 53 |
| Elongation at Break, % | 37 | |
| 34 |
| Poisson's Ratio | 0.37 | |
| 0.35 |
| Shear Modulus, GPa | 14 | |
| 20 |
Thermal Properties
| Latent Heat of Fusion, J/g | 47 | |
| 70 |
| Melting Completion (Liquidus), °C | 150 | |
| 370 |
| Melting Onset (Solidus), °C | 150 | |
| 220 |
| Specific Heat Capacity, J/kg-K | 190 | |
| 230 |
| Thermal Conductivity, W/m-K | 44 | |
| 45 |
| Thermal Expansion, µm/m-K | 26 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 10 | |
| 13 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 10 | |
| 16 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.8 | |
| 7.3 |
| Embodied Carbon, kg CO2/kg material | 9.2 | |
| 12 |
| Embodied Energy, MJ/kg | 160 | |
| 200 |
| Embodied Water, L/kg | 920 | |
| 1160 |
Common Calculations
| Stiffness to Weight: Axial, points | 2.5 | |
| 4.0 |
| Stiffness to Weight: Bending, points | 13 | |
| 17 |
| Thermal Diffusivity, mm2/s | 26 | |
| 26 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 to 0.2 | |
| 4.0 to 5.0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 to 0.1 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 to 0.080 |
| Cadmium (Cd), % | 17.5 to 18.5 | |
| 0 to 0.050 |
| Copper (Cu), % | 0 to 0.080 | |
| 4.0 to 5.0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.080 |
| Lead (Pb), % | 30.3 to 33 | |
| 0 to 0.35 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 49.5 to 50.5 | |
| 89.3 to 92 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 to 0.0050 |