Solder Alloy 182 vs. 50Cr-50Ni Alloy
Both solder alloy 182 and 50Cr-50Ni alloy are otherwise unclassified metals. Both are furnished in the as-fabricated (no temper or treatment) condition. There are 16 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is solder alloy 182 and the bottom bar is 50Cr-50Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 19 | |
| 210 |
| Elongation at Break, % | 37 | |
| 5.7 |
| Poisson's Ratio | 0.44 | |
| 0.26 |
| Shear Modulus, GPa | 6.7 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 28 | |
| 620 |
Thermal Properties
| Latent Heat of Fusion, J/g | 28 | |
| 350 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 490 |
| Thermal Expansion, µm/m-K | 29 | |
| 15 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 8.0 |
| Embodied Carbon, kg CO2/kg material | 9.0 | |
| 7.9 |
| Embodied Energy, MJ/kg | 140 | |
| 110 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.95 | |
| 15 |
| Stiffness to Weight: Bending, points | 7.9 | |
| 25 |
| Strength to Weight: Axial, points | 0.69 | |
| 21 |
| Strength to Weight: Bending, points | 1.8 | |
| 20 |
| Thermal Shock Resistance, points | 3.7 | |
| 14 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 to 0.25 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.1 |
| Chromium (Cr), % | 0 | |
| 48 to 52 |
| Copper (Cu), % | 0 to 0.080 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 1.0 |
| Lead (Pb), % | 93.2 to 95 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 to 0.010 | |
| 44.5 to 52 |
| Nitrogen (N), % | 0 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 5.0 to 6.0 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 0 to 0.25 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |