Solder Alloy 182 vs. C18600 Copper
Solder alloy 182 belongs to the otherwise unclassified metals classification, while C18600 copper belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is solder alloy 182 and the bottom bar is C18600 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 19 | |
| 120 |
| Elongation at Break, % | 37 | |
| 8.0 to 11 |
| Poisson's Ratio | 0.44 | |
| 0.34 |
| Shear Modulus, GPa | 6.7 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 28 | |
| 520 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 28 | |
| 210 |
| Melting Completion (Liquidus), °C | 370 | |
| 1090 |
| Melting Onset (Solidus), °C | 300 | |
| 1070 |
| Specific Heat Capacity, J/kg-K | 130 | |
| 390 |
| Thermal Conductivity, W/m-K | 27 | |
| 280 |
| Thermal Expansion, µm/m-K | 29 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 9.6 | |
| 70 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.6 | |
| 71 |
Otherwise Unclassified Properties
| Density, g/cm3 | 11 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 9.0 | |
| 2.9 |
| Embodied Energy, MJ/kg | 140 | |
| 46 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.95 | |
| 7.3 |
| Stiffness to Weight: Bending, points | 7.9 | |
| 18 |
| Strength to Weight: Axial, points | 0.69 | |
| 16 to 18 |
| Strength to Weight: Bending, points | 1.8 | |
| 16 to 17 |
| Thermal Diffusivity, mm2/s | 18 | |
| 81 |
| Thermal Shock Resistance, points | 3.7 | |
| 19 to 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.2 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0.1 to 1.0 |
| Cobalt (Co), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.080 | |
| 96.5 to 99.55 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0.25 to 0.8 |
| Lead (Pb), % | 93.2 to 95 | |
| 0 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.25 |
| Silver (Ag), % | 5.0 to 6.0 | |
| 0 |
| Tin (Sn), % | 0 to 0.25 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0.050 to 0.5 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 0.050 to 0.4 |
| Residuals, % | 0 | |
| 0 to 0.5 |