Both solder alloy 201 and 90-silver 10-cadmium-oxide are otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is solder alloy 201 and the bottom bar is 90-silver 10-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.3 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 12 | |
| 72 to 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 15 | |
| 64 to 91 |
| Elongation at Break, % | 38 | |
| 1.1 to 28 |
| Strength to Weight: Axial, points | 1.6 | |
| 7.0 to 11 |
| Strength to Weight: Bending, points | 3.6 | |
| 8.8 to 12 |
| Tensile Strength: Ultimate (UTS), MPa | 41 | |
| 260 to 400 |