Solder Alloy 401 vs. 80-silver 20-cadmium-oxide
Both solder alloy 401 and 80-silver 20-cadmium-oxide are otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is solder alloy 401 and the bottom bar is 80-silver 20-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.3 | |
| 9.9 |
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 63 to 77 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 57 to 70 |
| Elongation at Break, % | 21 | |
| 1.1 to 15 |
| Strength to Weight: Axial, points | 1.1 | |
| 8.8 to 12 |
| Strength to Weight: Bending, points | 2.9 | |
| 10 to 13 |
| Tensile Strength: Ultimate (UTS), MPa | 29 | |
| 310 to 440 |