Solder Alloy 401 vs. 86.5-silver 13.5-cadmium-oxide
Both solder alloy 401 and 86.5-silver 13.5-cadmium-oxide are otherwise unclassified metals. There are 7 material properties with values for both materials. Properties with values for just one material (18, in this case) are not shown.
For each property being compared, the top bar is solder alloy 401 and the bottom bar is 86.5-silver 13.5-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 7.3 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 72 to 85 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 64 to 76 |
| Elongation at Break, % | 21 | |
| 3.4 to 16 |
| Strength to Weight: Axial, points | 1.1 | |
| 7.6 to 11 |
| Strength to Weight: Bending, points | 2.9 | |
| 9.3 to 12 |
| Tensile Strength: Ultimate (UTS), MPa | 29 | |
| 280 to 410 |