Solder Alloy 501 vs. S32205 Stainless Steel
Solder alloy 501 belongs to the otherwise unclassified metals classification, while S32205 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is solder alloy 501 and the bottom bar is S32205 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 14 | |
| 260 |
| Elastic (Young's, Tensile) Modulus, GPa | 51 | |
| 200 |
| Elongation at Break, % | 22 | |
| 28 |
| Poisson's Ratio | 0.36 | |
| 0.27 |
| Shear Modulus, GPa | 19 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 29 | |
| 740 |
Thermal Properties
| Latent Heat of Fusion, J/g | 60 | |
| 300 |
| Melting Completion (Liquidus), °C | 230 | |
| 1450 |
| Melting Onset (Solidus), °C | 220 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 220 | |
| 480 |
| Thermal Conductivity, W/m-K | 67 | |
| 15 |
| Thermal Expansion, µm/m-K | 22 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 14 | |
| 2.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 2.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.3 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 15 | |
| 3.7 |
| Embodied Energy, MJ/kg | 260 | |
| 50 |
| Embodied Water, L/kg | 1390 | |
| 160 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 17 | |
| 25 |
| Strength to Weight: Axial, points | 1.1 | |
| 26 |
| Strength to Weight: Bending, points | 2.9 | |
| 23 |
| Thermal Diffusivity, mm2/s | 41 | |
| 4.0 |
| Thermal Shock Resistance, points | 1.9 | |
| 20 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.060 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 22 to 23 |
| Copper (Cu), % | 0.5 to 0.9 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 63.7 to 70.4 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 | |
| 3.0 to 3.5 |
| Nickel (Ni), % | 0 to 0.010 | |
| 4.5 to 6.5 |
| Nitrogen (N), % | 0 | |
| 0.14 to 0.2 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0 to 1.0 |
| Silver (Ag), % | 0.2 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 98.3 to 99.3 | |
| 0 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |