Solder Alloy 704 vs. Austempered Cast Iron
Solder alloy 704 belongs to the otherwise unclassified metals classification, while austempered cast iron belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is solder alloy 704 and the bottom bar is austempered cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 14 | |
| 270 to 490 |
| Elastic (Young's, Tensile) Modulus, GPa | 51 | |
| 180 |
| Elongation at Break, % | 30 | |
| 1.1 to 13 |
| Poisson's Ratio | 0.36 | |
| 0.29 |
| Shear Modulus, GPa | 19 | |
| 62 to 69 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 860 to 1800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 62 | |
| 280 |
| Melting Completion (Liquidus), °C | 240 | |
| 1380 |
| Melting Onset (Solidus), °C | 220 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 220 | |
| 490 |
| Thermal Conductivity, W/m-K | 50 | |
| 42 |
| Thermal Expansion, µm/m-K | 22 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.5 | |
| 7.5 |
| Embodied Carbon, kg CO2/kg material | 19 | |
| 1.8 |
| Embodied Energy, MJ/kg | 320 | |
| 25 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 13 |
| Stiffness to Weight: Bending, points | 17 | |
| 25 |
| Strength to Weight: Axial, points | 2.1 | |
| 32 to 66 |
| Strength to Weight: Bending, points | 4.3 | |
| 27 to 44 |
| Thermal Diffusivity, mm2/s | 30 | |
| 11 |
| Thermal Shock Resistance, points | 3.5 | |
| 25 to 53 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 to 0.050 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 to 0.020 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 3.4 to 3.8 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.8 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 89.6 to 94 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Magnesium (Mg), % | 0 | |
| 0 to 0.040 |
| Manganese (Mn), % | 0 | |
| 0.3 to 0.4 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.3 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 2.0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Selenium (Se), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 2.3 to 2.7 |
| Silver (Ag), % | 4.8 to 5.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.020 |
| Tin (Sn), % | 94.3 to 95.2 | |
| 0 to 0.020 |
| Vanadium (V), % | 0 | |
| 0 to 0.1 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |