Solder Alloy 704 vs. SAE-AISI H13 Steel
Solder alloy 704 belongs to the otherwise unclassified metals classification, while SAE-AISI H13 steel belongs to the iron alloys. There are 21 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is solder alloy 704 and the bottom bar is SAE-AISI H13 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 51 | |
| 190 |
| Poisson's Ratio | 0.36 | |
| 0.29 |
| Shear Modulus, GPa | 19 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 690 to 1820 |
Thermal Properties
| Latent Heat of Fusion, J/g | 62 | |
| 270 |
| Melting Completion (Liquidus), °C | 240 | |
| 1460 |
| Melting Onset (Solidus), °C | 220 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 220 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 29 |
| Thermal Expansion, µm/m-K | 22 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 13 | |
| 8.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 15 | |
| 9.7 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.5 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 19 | |
| 4.3 |
| Embodied Energy, MJ/kg | 320 | |
| 64 |
Common Calculations
| Stiffness to Weight: Axial, points | 3.8 | |
| 14 |
| Stiffness to Weight: Bending, points | 17 | |
| 25 |
| Strength to Weight: Axial, points | 2.1 | |
| 25 to 65 |
| Strength to Weight: Bending, points | 4.3 | |
| 22 to 43 |
| Thermal Diffusivity, mm2/s | 30 | |
| 7.8 |
| Thermal Shock Resistance, points | 3.5 | |
| 25 to 65 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.32 to 0.45 |
| Chromium (Cr), % | 0 | |
| 4.8 to 5.5 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 to 0.25 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 88.8 to 92 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Manganese (Mn), % | 0 | |
| 0.2 to 0.5 |
| Molybdenum (Mo), % | 0 | |
| 1.1 to 1.8 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.3 |
| Phosphorus (P), % | 0 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 | |
| 0.8 to 1.2 |
| Silver (Ag), % | 4.8 to 5.2 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Tin (Sn), % | 94.3 to 95.2 | |
| 0 |
| Vanadium (V), % | 0 | |
| 0.8 to 1.2 |
| Zinc (Zn), % | 0 to 0.0010 | |
| 0 |