Solder Alloy 713 vs. S30601 Stainless Steel

Solder alloy 713 belongs to the otherwise unclassified metals classification, while S30601 stainless steel belongs to the iron alloys. There are 19 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is solder alloy 713 and the bottom bar is S30601 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 15
190
Elastic (Young's, Tensile) Modulus, GPa 51
190
Elongation at Break, % 16
37
Poisson's Ratio 0.36
0.28
Shear Modulus, GPa 19
75
Tensile Strength: Ultimate (UTS), MPa 59
660

Thermal Properties

Latent Heat of Fusion, J/g 62
370
Melting Completion (Liquidus), °C 220
1360
Melting Onset (Solidus), °C 220
1310
Specific Heat Capacity, J/kg-K 220
500
Thermal Expansion, µm/m-K 22
15

Otherwise Unclassified Properties

Density, g/cm3 7.4
7.6
Embodied Carbon, kg CO2/kg material 18
3.9
Embodied Energy, MJ/kg 300
55

Common Calculations

Stiffness to Weight: Axial, points 3.8
14
Stiffness to Weight: Bending, points 17
25
Strength to Weight: Axial, points 2.2
24
Strength to Weight: Bending, points 4.5
22
Thermal Shock Resistance, points 3.7
16

Alloy Composition

Aluminum (Al), % 0 to 0.0010
0
Antimony (Sb), % 0 to 0.1
0
Arsenic (As), % 0 to 0.030
0
Bismuth (Bi), % 0 to 0.1
0
Cadmium (Cd), % 0 to 0.0020
0
Carbon (C), % 0
0 to 0.015
Chromium (Cr), % 0
17 to 18
Copper (Cu), % 0.5 to 0.9
0 to 0.35
Gold (Au), % 0 to 0.050
0
Indium (In), % 0 to 0.1
0
Iron (Fe), % 0 to 0.020
56.9 to 60.5
Lead (Pb), % 0 to 0.070
0
Manganese (Mn), % 0
0.5 to 0.8
Molybdenum (Mo), % 0
0 to 0.2
Nickel (Ni), % 0 to 0.010
17 to 18
Nitrogen (N), % 0
0 to 0.050
Phosphorus (P), % 0
0 to 0.030
Silicon (Si), % 0
5.0 to 5.6
Silver (Ag), % 3.6 to 4.0
0
Sulfur (S), % 0
0 to 0.013
Tin (Sn), % 94.6 to 95.9
0
Zinc (Zn), % 0 to 0.0010
0