Solder Alloy 716 vs. Grade 200 Maraging Steel
Solder alloy 716 belongs to the otherwise unclassified metals classification, while grade 200 maraging steel belongs to the iron alloys. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is solder alloy 716 and the bottom bar is grade 200 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 51 | |
190 |
Elongation at Break, % | 13 | |
9.1 to 18 |
Poisson's Ratio | 0.36 | |
0.3 |
Shear Modulus, GPa | 19 | |
74 |
Tensile Strength: Ultimate (UTS), MPa | 39 | |
970 to 1500 |
Thermal Properties
Latent Heat of Fusion, J/g | 60 | |
260 |
Melting Completion (Liquidus), °C | 230 | |
1460 |
Melting Onset (Solidus), °C | 220 | |
1420 |
Specific Heat Capacity, J/kg-K | 220 | |
460 |
Thermal Expansion, µm/m-K | 22 | |
12 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.3 | |
8.2 |
Embodied Carbon, kg CO2/kg material | 16 | |
4.5 |
Embodied Energy, MJ/kg | 270 | |
59 |
Common Calculations
Stiffness to Weight: Axial, points | 3.8 | |
13 |
Stiffness to Weight: Bending, points | 17 | |
23 |
Strength to Weight: Axial, points | 1.5 | |
33 to 51 |
Strength to Weight: Bending, points | 3.5 | |
27 to 35 |
Thermal Shock Resistance, points | 2.5 | |
29 to 45 |
Alloy Composition
Aluminum (Al), % | 0 to 0.0010 | |
0.050 to 0.15 |
Antimony (Sb), % | 0 to 0.1 | |
0 |
Arsenic (As), % | 0 to 0.030 | |
0 |
Bismuth (Bi), % | 0 to 0.1 | |
0 |
Boron (B), % | 0 | |
0 to 0.0030 |
Cadmium (Cd), % | 0 to 0.0020 | |
0 |
Calcium (Ca), % | 0 | |
0 to 0.050 |
Carbon (C), % | 0 | |
0 to 0.030 |
Cobalt (Co), % | 0 | |
8.0 to 9.0 |
Copper (Cu), % | 0.3 to 0.7 | |
0 |
Gold (Au), % | 0 to 0.050 | |
0 |
Indium (In), % | 0 to 0.1 | |
0 |
Iron (Fe), % | 0 to 0.020 | |
67.8 to 71.8 |
Lead (Pb), % | 0 to 0.070 | |
0 |
Manganese (Mn), % | 0 | |
0 to 0.1 |
Molybdenum (Mo), % | 0 | |
3.0 to 3.5 |
Nickel (Ni), % | 0 to 0.010 | |
17 to 19 |
Phosphorus (P), % | 0 | |
0 to 0.010 |
Silicon (Si), % | 0 | |
0 to 0.1 |
Silver (Ag), % | 0.8 to 1.2 | |
0 |
Sulfur (S), % | 0 | |
0 to 0.010 |
Tin (Sn), % | 97.6 to 98.9 | |
0 |
Titanium (Ti), % | 0 | |
0.15 to 0.25 |
Zinc (Zn), % | 0 to 0.0010 | |
0 |
Zirconium (Zr), % | 0 | |
0 to 0.020 |