Solder Alloy 801 vs. C84100 Brass
Solder alloy 801 belongs to the otherwise unclassified metals classification, while C84100 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is solder alloy 801 and the bottom bar is C84100 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 22 | |
| 65 |
| Elastic (Young's, Tensile) Modulus, GPa | 53 | |
| 110 |
| Elongation at Break, % | 33 | |
| 13 |
| Poisson's Ratio | 0.35 | |
| 0.33 |
| Shear Modulus, GPa | 20 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 64 | |
| 190 |
| Melting Completion (Liquidus), °C | 200 | |
| 1000 |
| Melting Onset (Solidus), °C | 200 | |
| 810 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 380 |
| Thermal Conductivity, W/m-K | 61 | |
| 110 |
| Thermal Expansion, µm/m-K | 22 | |
| 19 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 23 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 25 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.2 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 14 | |
| 2.9 |
| Embodied Energy, MJ/kg | 240 | |
| 48 |
| Embodied Water, L/kg | 1140 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 17 | |
| 19 |
| Strength to Weight: Axial, points | 2.1 | |
| 7.4 |
| Strength to Weight: Bending, points | 4.4 | |
| 9.7 |
| Thermal Diffusivity, mm2/s | 36 | |
| 33 |
| Thermal Shock Resistance, points | 3.3 | |
| 7.8 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 to 0.010 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 to 0.050 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 to 0.090 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Copper (Cu), % | 0 to 0.050 | |
| 78 to 85 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.3 |
| Lead (Pb), % | 0 to 0.070 | |
| 0.050 to 0.25 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.5 |
| Phosphorus (P), % | 0 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 | |
| 0 to 0.010 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tin (Sn), % | 89.9 to 91.5 | |
| 1.5 to 4.5 |
| Zinc (Zn), % | 8.5 to 9.5 | |
| 12 to 20 |
| Residuals, % | 0 | |
| 0 to 0.5 |