Solder Alloy 801 vs. R05240 Alloy
Both solder alloy 801 and R05240 alloy are otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is solder alloy 801 and the bottom bar is R05240 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 53 | |
| 150 |
| Elongation at Break, % | 33 | |
| 25 |
| Poisson's Ratio | 0.35 | |
| 0.36 |
| Shear Modulus, GPa | 20 | |
| 57 |
| Tensile Strength: Ultimate (UTS), MPa | 55 | |
| 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 64 | |
| 210 |
| Specific Heat Capacity, J/kg-K | 240 | |
| 190 |
| Thermal Expansion, µm/m-K | 22 | |
| 6.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.2 | |
| 14 |
| Embodied Water, L/kg | 1140 | |
| 460 |
Common Calculations
| Stiffness to Weight: Axial, points | 4.1 | |
| 6.3 |
| Stiffness to Weight: Bending, points | 17 | |
| 13 |
| Strength to Weight: Axial, points | 2.1 | |
| 5.4 |
| Strength to Weight: Bending, points | 4.4 | |
| 6.8 |
| Thermal Shock Resistance, points | 3.3 | |
| 18 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.0010 | |
| 0 |
| Antimony (Sb), % | 0 to 0.1 | |
| 0 |
| Arsenic (As), % | 0 to 0.030 | |
| 0 |
| Bismuth (Bi), % | 0 to 0.1 | |
| 0 |
| Cadmium (Cd), % | 0 to 0.0020 | |
| 0 |
| Carbon (C), % | 0 | |
| 0 to 0.010 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Gold (Au), % | 0 to 0.050 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Indium (In), % | 0 to 0.1 | |
| 0 |
| Iron (Fe), % | 0 to 0.020 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 to 0.070 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.020 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.010 |
| Niobium (Nb), % | 0 | |
| 35 to 42 |
| Nitrogen (N), % | 0 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.020 |
| Silicon (Si), % | 0 | |
| 0 to 0.0050 |
| Silver (Ag), % | 0 to 0.1 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 57.9 to 65 |
| Tin (Sn), % | 89.9 to 91.5 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |
| Zinc (Zn), % | 8.5 to 9.5 | |
| 0 |