ISO-WD21150 Magnesium vs. AISI 205 Stainless Steel
ISO-WD21150 magnesium belongs to the magnesium alloys classification, while AISI 205 stainless steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is ISO-WD21150 magnesium and the bottom bar is AISI 205 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 200 |
| Elongation at Break, % | 5.7 to 11 | |
| 11 to 51 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 17 | |
| 77 |
| Shear Strength, MPa | 150 to 170 | |
| 560 to 850 |
| Tensile Strength: Ultimate (UTS), MPa | 240 to 290 | |
| 800 to 1430 |
| Tensile Strength: Yield (Proof), MPa | 120 to 200 | |
| 450 to 1100 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 110 | |
| 880 |
| Melting Completion (Liquidus), °C | 600 | |
| 1380 |
| Melting Onset (Solidus), °C | 550 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 480 |
| Thermal Expansion, µm/m-K | 27 | |
| 18 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 11 |
| Density, g/cm3 | 1.7 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 2.6 |
| Embodied Energy, MJ/kg | 160 | |
| 37 |
| Embodied Water, L/kg | 980 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 15 to 24 | |
| 150 to 430 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 460 | |
| 510 to 3060 |
| Stiffness to Weight: Axial, points | 15 | |
| 14 |
| Stiffness to Weight: Bending, points | 70 | |
| 26 |
| Strength to Weight: Axial, points | 40 to 48 | |
| 29 to 52 |
| Strength to Weight: Bending, points | 52 to 58 | |
| 25 to 37 |
| Thermal Shock Resistance, points | 15 to 17 | |
| 16 to 29 |
Alloy Composition
| Aluminum (Al), % | 2.4 to 3.6 | |
| 0 |
| Carbon (C), % | 0 | |
| 0.12 to 0.25 |
| Chromium (Cr), % | 0 | |
| 16.5 to 18.5 |
| Copper (Cu), % | 0 to 0.050 | |
| 0 |
| Iron (Fe), % | 0 to 0.0050 | |
| 62.6 to 68.1 |
| Magnesium (Mg), % | 94 to 97 | |
| 0 |
| Manganese (Mn), % | 0.15 to 0.4 | |
| 14 to 15.5 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 1.0 to 1.7 |
| Nitrogen (N), % | 0 | |
| 0.32 to 0.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.060 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 | |
| 0 to 0.030 |
| Zinc (Zn), % | 0.5 to 1.5 | |
| 0 |
| Residuals, % | 0 to 0.3 | |
| 0 |