ISO-WD32350 Magnesium vs. 7050 Aluminum
ISO-WD32350 magnesium belongs to the magnesium alloys classification, while 7050 aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is ISO-WD32350 magnesium and the bottom bar is 7050 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 70 |
| Elongation at Break, % | 5.7 to 10 | |
| 2.2 to 12 |
| Fatigue Strength, MPa | 120 to 130 | |
| 130 to 210 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 18 | |
| 26 |
| Shear Strength, MPa | 150 to 170 | |
| 280 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 290 | |
| 490 to 570 |
| Tensile Strength: Yield (Proof), MPa | 140 to 180 | |
| 390 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 340 | |
| 370 |
| Maximum Temperature: Mechanical, °C | 95 | |
| 190 |
| Melting Completion (Liquidus), °C | 600 | |
| 630 |
| Melting Onset (Solidus), °C | 560 | |
| 490 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 860 |
| Thermal Conductivity, W/m-K | 130 | |
| 140 |
| Thermal Expansion, µm/m-K | 25 | |
| 24 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 35 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 130 | |
| 100 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 10 |
| Density, g/cm3 | 1.7 | |
| 3.1 |
| Embodied Carbon, kg CO2/kg material | 23 | |
| 8.2 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 960 | |
| 1120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 23 | |
| 10 to 55 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 380 | |
| 1110 to 1760 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 68 | |
| 45 |
| Strength to Weight: Axial, points | 39 to 46 | |
| 45 to 51 |
| Strength to Weight: Bending, points | 50 to 55 | |
| 45 to 50 |
| Thermal Diffusivity, mm2/s | 73 | |
| 54 |
| Thermal Shock Resistance, points | 16 to 18 | |
| 21 to 25 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.1 | |
| 87.3 to 92.1 |
| Chromium (Cr), % | 0 | |
| 0 to 0.040 |
| Copper (Cu), % | 0 to 0.1 | |
| 2.0 to 2.6 |
| Iron (Fe), % | 0 to 0.060 | |
| 0 to 0.15 |
| Magnesium (Mg), % | 95.7 to 97.7 | |
| 1.9 to 2.6 |
| Manganese (Mn), % | 0.6 to 1.3 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.0050 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.12 |
| Titanium (Ti), % | 0 | |
| 0 to 0.060 |
| Zinc (Zn), % | 1.8 to 2.3 | |
| 5.7 to 6.7 |
| Zirconium (Zr), % | 0 | |
| 0.080 to 0.15 |
| Residuals, % | 0 | |
| 0 to 0.15 |