ISO-WD32350 Magnesium vs. 88-silver 12-tin-oxide
ISO-WD32350 magnesium belongs to the magnesium alloys classification, while 88-silver 12-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is ISO-WD32350 magnesium and the bottom bar is 88-silver 12-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 84 to 86 |
| Elongation at Break, % | 5.7 to 10 | |
| 9.0 to 37 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 23 | |
| 24 to 70 |
| Shear Strength, MPa | 150 to 170 | |
| 150 to 160 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 290 | |
| 230 to 280 |
| Tensile Strength: Yield (Proof), MPa | 140 to 180 | |
| 110 to 260 |