ISO-WD32350 Magnesium vs. 90-silver 10-tin-oxide
ISO-WD32350 magnesium belongs to the magnesium alloys classification, while 90-silver 10-tin-oxide belongs to the otherwise unclassified metals. There are 6 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is ISO-WD32350 magnesium and the bottom bar is 90-silver 10-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
| Electrical Conductivity: Equal Volume, % IACS | 25 | |
| 77 to 82 |
| Elongation at Break, % | 5.7 to 10 | |
| 7.0 to 35 |
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 14 to 23 | |
| 20 to 68 |
| Shear Strength, MPa | 150 to 170 | |
| 160 to 170 |
| Tensile Strength: Ultimate (UTS), MPa | 250 to 290 | |
| 230 to 300 |
| Tensile Strength: Yield (Proof), MPa | 140 to 180 | |
| 120 to 280 |