IR Rubber vs. PA 6/12
IR rubber belongs to the thermoset elastomers (rubber) classification, while PA 6/12 belongs to the thermoplastics. There are 10 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is IR rubber and the bottom bar is PA 6/12.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 1.0 | |
| 1.1 |
| Elongation at Break, % | 600 | |
| 30 to 120 |
| Limiting Oxygen Index (LOI), % | 19 | |
| 25 |
| Maximum Temperature: Decomposition, °C | 300 | |
| 450 |
| Specific Heat Capacity, J/kg-K | 1550 | |
| 1590 |
| Strength to Weight: Axial, points | 5.6 | |
| 10 to 15 |
| Strength to Weight: Bending, points | 17 | |
| 25 to 31 |
| Tensile Strength: Ultimate (UTS), MPa | 19 | |
| 40 to 58 |
| Thermal Conductivity, W/m-K | 0.14 | |
| 0.22 |
| Thermal Diffusivity, mm2/s | 0.1 | |
| 0.13 |