Lithium Fluoride vs. Alumina
Lithium fluoride belongs to the non-glass optical ceramics classification, while alumina belongs to the oxide-based engineering ceramics. There are 12 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is lithium fluoride and the bottom bar is alumina.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 120 | |
| 220 to 370 |
| Poisson's Ratio | 0.27 | |
| 0.22 to 0.24 |
Thermal Properties
| Melting Onset (Solidus), °C | 870 | |
| 2040 |
| Specific Heat Capacity, J/kg-K | 1560 | |
| 870 to 940 |
| Thermal Conductivity, W/m-K | 12 | |
| 14 to 30 |
| Thermal Expansion, µm/m-K | 32 | |
| 6.7 to 8.2 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 9.0 | |
| 7.8 to 11 |
| Electrical Dissipation At 1 MHz | 0.00020 | |
| 0.00049 to 0.0013 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.6 | |
| 3.4 to 4.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 24 | |
| 35 to 53 |
| Stiffness to Weight: Bending, points | 62 | |
| 57 to 62 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 3.7 to 10 |