Lithium Fluoride vs. C-310 Titania-based Ceramic
Lithium fluoride belongs to the non-glass optical ceramics classification, while C-310 titania-based ceramic belongs to the oxide-based engineering ceramics. There are 6 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is lithium fluoride and the bottom bar is C-310 titania-based ceramic.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 2.6 | |
| 3.7 |
| Electrical Dissipation At 1 MHz | 0.00020 | |
| 0.0018 |
| Specific Heat Capacity, J/kg-K | 1560 | |
| 750 |
| Thermal Conductivity, W/m-K | 12 | |
| 3.5 |
| Thermal Diffusivity, mm2/s | 2.9 | |
| 1.3 |
| Thermal Expansion, µm/m-K | 32 | |
| 7.0 |