R31537 Cobalt vs. SAE-AISI 1055 Steel
R31537 cobalt belongs to the cobalt alloys classification, while SAE-AISI 1055 steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is R31537 cobalt and the bottom bar is SAE-AISI 1055 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 190 |
| Elongation at Break, % | 14 to 23 | |
| 11 to 14 |
| Fatigue Strength, MPa | 310 to 480 | |
| 260 to 390 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 13 to 23 | |
| 34 to 45 |
| Shear Modulus, GPa | 87 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 1000 to 1340 | |
| 730 to 750 |
| Tensile Strength: Yield (Proof), MPa | 590 to 940 | |
| 400 to 630 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 250 |
| Melting Completion (Liquidus), °C | 1360 | |
| 1460 |
| Melting Onset (Solidus), °C | 1290 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 13 | |
| 51 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.1 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 8.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 110 | |
| 18 |
| Embodied Water, L/kg | 530 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 to 200 | |
| 80 to 85 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 780 to 1990 | |
| 440 to 1070 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 33 to 44 | |
| 26 |
| Strength to Weight: Bending, points | 26 to 32 | |
| 23 |
| Thermal Diffusivity, mm2/s | 3.4 | |
| 14 |
| Thermal Shock Resistance, points | 24 to 32 | |
| 23 to 24 |
Alloy Composition
| Carbon (C), % | 0 to 0.14 | |
| 0.5 to 0.6 |
| Chromium (Cr), % | 26 to 30 | |
| 0 |
| Cobalt (Co), % | 58.9 to 69 | |
| 0 |
| Iron (Fe), % | 0 to 0.75 | |
| 98.4 to 98.9 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 5.0 to 7.0 | |
| 0 |
| Nickel (Ni), % | 0 to 1.0 | |
| 0 |
| Nitrogen (N), % | 0 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 | |
| 0 to 0.050 |