LDPE vs. PLA
Both LDPE and PLA are thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is LDPE and the bottom bar is PLA.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 0.3 | |
3.5 |
Shear Modulus, GPa | 0.21 | |
2.4 |
Tensile Strength: Ultimate (UTS), MPa | 7.0 | |
50 |
Thermal Properties
Glass Transition Temperature, °C | -130 | |
60 |
Melting Onset (Solidus), °C | 110 | |
160 |
Specific Heat Capacity, J/kg-K | 2300 | |
1800 |
Thermal Conductivity, W/m-K | 0.36 | |
0.13 |
Otherwise Unclassified Properties
Density, g/cm3 | 0.92 | |
1.3 |
Common Calculations
Stiffness to Weight: Axial, points | 0.18 | |
1.6 |
Stiffness to Weight: Bending, points | 24 | |
40 |
Strength to Weight: Axial, points | 2.1 | |
11 |
Strength to Weight: Bending, points | 8.8 | |
24 |
Thermal Diffusivity, mm2/s | 0.17 | |
0.058 |