LDPE vs. PS
Both LDPE and PS are thermoplastics. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is LDPE and the bottom bar is PS.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 0.3 | |
| 1.9 to 2.9 |
| Tensile Strength: Ultimate (UTS), MPa | 7.0 | |
| 32 to 44 |
Thermal Properties
| Glass Transition Temperature, °C | -130 | |
| 100 |
| Maximum Temperature: Autoignition, °C | 380 | |
| 360 to 420 |
| Maximum Temperature: Decomposition, °C | 400 | |
| 320 to 330 |
| Specific Heat Capacity, J/kg-K | 2300 | |
| 1250 to 1400 |
| Thermal Conductivity, W/m-K | 0.36 | |
| 0.14 to 0.22 |
| Thermal Expansion, µm/m-K | 220 | |
| 80 to 98 |
| Vicat Softening Temperature, °C | 50 | |
| 100 to 110 |
Otherwise Unclassified Properties
| Density, g/cm3 | 0.92 | |
| 1.0 |
Common Calculations
| Stiffness to Weight: Axial, points | 0.18 | |
| 1.0 to 1.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 40 to 45 |
| Strength to Weight: Axial, points | 2.1 | |
| 8.5 to 12 |
| Strength to Weight: Bending, points | 8.8 | |
| 22 to 26 |
| Thermal Diffusivity, mm2/s | 0.17 | |
| 0.11 to 0.15 |
| Thermal Shock Resistance, points | 7.6 | |
| 11 to 15 |