Low Expansion Glass-ceramic vs. Beryllia
Low expansion glass-ceramic belongs to the glass and glass-ceramics classification, while beryllia belongs to the oxide-based engineering ceramics. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is low expansion glass-ceramic and the bottom bar is beryllia.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 350 |
| Flexural Strength, MPa | 35 | |
| 240 |
| Poisson's Ratio | 0.22 | |
| 0.26 |
| Tensile Strength: Ultimate (UTS), MPa | 53 | |
| 140 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 690 | |
| 1750 |
| Specific Heat Capacity, J/kg-K | 800 | |
| 1050 |
| Thermal Conductivity, W/m-K | 1.5 | |
| 270 |
| Thermal Expansion, µm/m-K | 1.7 | |
| 8.0 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 5.7 | |
| 6.6 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 11 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.4 | |
| 2.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 19 | |
| 67 |
| Stiffness to Weight: Bending, points | 59 | |
| 82 |
| Strength to Weight: Axial, points | 6.1 | |
| 14 |
| Strength to Weight: Bending, points | 13 | |
| 21 |
| Thermal Diffusivity, mm2/s | 0.76 | |
| 89 |
| Thermal Shock Resistance, points | 28 | |
| 3.6 |