Low Expansion Glass-ceramic vs. Silicon Nitride
Low expansion glass-ceramic belongs to the glass and glass-ceramics classification, while silicon nitride belongs to the non-oxide engineering ceramics. There are 13 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is low expansion glass-ceramic and the bottom bar is silicon nitride.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 140 to 310 |
| Flexural Strength, MPa | 35 | |
| 130 to 810 |
| Poisson's Ratio | 0.22 | |
| 0.24 to 0.27 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 690 | |
| 1000 to 1330 |
| Specific Heat Capacity, J/kg-K | 800 | |
| 720 to 800 |
| Thermal Conductivity, W/m-K | 1.5 | |
| 12 to 31 |
| Thermal Expansion, µm/m-K | 1.7 | |
| 2.5 to 3.2 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 5.7 | |
| 8.0 to 10 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 11 | |
| 11 to 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.4 | |
| 2.2 to 3.4 |
Common Calculations
| Stiffness to Weight: Axial, points | 19 | |
| 34 to 53 |
| Stiffness to Weight: Bending, points | 59 | |
| 65 to 78 |
| Thermal Diffusivity, mm2/s | 0.76 | |
| 7.5 to 13 |