Low Expansion Glass-ceramic vs. Zinc Sulfide
Low expansion glass-ceramic belongs to the glass and glass-ceramics classification, while zinc sulfide belongs to the non-glass optical ceramics. There are 11 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is low expansion glass-ceramic and the bottom bar is zinc sulfide.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 83 | |
| 75 |
| Poisson's Ratio | 0.22 | |
| 0.28 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 800 | |
| 520 |
| Thermal Conductivity, W/m-K | 1.5 | |
| 27 |
| Thermal Expansion, µm/m-K | 1.7 | |
| 6.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.4 | |
| 4.1 |
| Light Transmission Range, µm | 0.5 to 2.7 | |
| 0.37 to 14 |
| Refractive Index | 1.5 | |
| 2.3 |
Common Calculations
| Stiffness to Weight: Axial, points | 19 | |
| 10 |
| Stiffness to Weight: Bending, points | 59 | |
| 34 |
| Thermal Diffusivity, mm2/s | 0.76 | |
| 13 |