M1A Magnesium vs. 2014A Aluminum
M1A magnesium belongs to the magnesium alloys classification, while 2014A aluminum belongs to the aluminum alloys.
For each property being compared, the top bar is M1A magnesium and the bottom bar is 2014A aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 45 | |
| 72 |
| Elongation at Break, % | 5.5 | |
| 6.2 to 16 |
| Fatigue Strength, MPa | 88 | |
| 93 to 150 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 18 | |
| 27 |
| Shear Strength, MPa | 120 | |
| 130 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 230 | |
| 210 to 490 |
| Tensile Strength: Yield (Proof), MPa | 130 | |
| 110 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 350 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 95 | |
| 210 |
| Melting Completion (Liquidus), °C | 610 | |
| 640 |
| Melting Onset (Solidus), °C | 580 | |
| 510 |
| Specific Heat Capacity, J/kg-K | 990 | |
| 870 |
| Thermal Conductivity, W/m-K | 150 | |
| 150 |
| Thermal Expansion, µm/m-K | 26 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 35 | |
| 37 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 190 | |
| 110 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 11 |
| Density, g/cm3 | 1.7 | |
| 3.0 |
| Embodied Carbon, kg CO2/kg material | 24 | |
| 8.1 |
| Embodied Energy, MJ/kg | 160 | |
| 150 |
| Embodied Water, L/kg | 970 | |
| 1140 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 11 | |
| 24 to 49 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 180 | |
| 85 to 1300 |
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 71 | |
| 46 |
| Strength to Weight: Axial, points | 38 | |
| 19 to 45 |
| Strength to Weight: Bending, points | 49 | |
| 26 to 46 |
| Thermal Diffusivity, mm2/s | 88 | |
| 55 |
| Thermal Shock Resistance, points | 13 | |
| 9.0 to 22 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 90.8 to 95 |
| Calcium (Ca), % | 0 to 0.3 | |
| 0 |
| Chromium (Cr), % | 0 | |
| 0 to 0.1 |
| Copper (Cu), % | 0 to 0.050 | |
| 3.9 to 5.0 |
| Iron (Fe), % | 0 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 97.2 to 98.8 | |
| 0.2 to 0.8 |
| Manganese (Mn), % | 1.2 to 2.0 | |
| 0.4 to 1.2 |
| Nickel (Ni), % | 0 to 0.010 | |
| 0 to 0.1 |
| Silicon (Si), % | 0 to 0.1 | |
| 0.5 to 0.9 |
| Titanium (Ti), % | 0 | |
| 0 to 0.15 |
| Zinc (Zn), % | 0 | |
| 0 to 0.25 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |