Machinable Glass-ceramic vs. Barium Fluoride
Machinable glass-ceramic belongs to the glass and glass-ceramics classification, while barium fluoride belongs to the non-glass optical ceramics. There are 11 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is machinable glass-ceramic and the bottom bar is barium fluoride.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 60 |
| Knoop Hardness | 250 | |
| 80 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 26 | |
| 25 |
Thermal Properties
| Specific Heat Capacity, J/kg-K | 790 | |
| 420 |
| Thermal Conductivity, W/m-K | 1.2 | |
| 9.0 |
| Thermal Expansion, µm/m-K | 21 | |
| 18 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 4.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 51 | |
| 27 |
| Thermal Diffusivity, mm2/s | 0.56 | |
| 4.4 |