Machinable Glass-ceramic vs. Cordierite
Machinable glass-ceramic belongs to the glass and glass-ceramics classification, while cordierite belongs to the oxide-based engineering ceramics. There are 19 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is machinable glass-ceramic and the bottom bar is cordierite.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 310 | |
| 420 |
| Elastic (Young's, Tensile) Modulus, GPa | 67 | |
| 62 |
| Flexural Strength, MPa | 96 | |
| 17 to 32 |
| Fracture Toughness, MPa-m1/2 | 2.5 | |
| 2.0 |
| Tensile Strength: Ultimate (UTS), MPa | 84 | |
| 190 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 760 | |
| 1150 |
| Specific Heat Capacity, J/kg-K | 790 | |
| 800 to 850 |
| Thermal Conductivity, W/m-K | 1.2 | |
| 1.3 to 1.7 |
| Thermal Expansion, µm/m-K | 21 | |
| 2.9 to 4.8 |
Electrical Properties
| Dielectric Constant (Relative Permittivity) At 1 MHz | 6.4 | |
| 4.7 |
| Dielectric Strength (Breakdown Potential), kV/mm | 27 | |
| 7.7 |
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 14 | |
| 9.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 | |
| 2.0 to 2.2 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 15 to 17 |
| Stiffness to Weight: Bending, points | 51 | |
| 59 to 67 |
| Strength to Weight: Axial, points | 8.8 | |
| 24 to 27 |
| Strength to Weight: Bending, points | 16 | |
| 33 to 38 |
| Thermal Diffusivity, mm2/s | 0.56 | |
| 0.74 to 1.0 |
| Thermal Shock Resistance, points | 4.3 | |
| 47 to 78 |