Melamine vs. PA 6/10
Melamine belongs to the thermoset plastics classification, while PA 6/10 belongs to the thermoplastics. There are 13 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is melamine and the bottom bar is PA 6/10.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 7.0 | |
| 1.6 to 2.3 |
| Elongation at Break, % | 1.0 | |
| 110 to 120 |
| Tensile Strength: Ultimate (UTS), MPa | 30 | |
| 45 to 60 |
Thermal Properties
| Maximum Temperature: Decomposition, °C | 350 | |
| 440 |
| Specific Heat Capacity, J/kg-K | 1200 | |
| 1510 |
| Thermal Conductivity, W/m-K | 0.5 | |
| 0.23 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 30 | |
| 15 to 19 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.5 | |
| 1.1 |
Common Calculations
| Stiffness to Weight: Axial, points | 2.6 | |
| 0.78 to 1.1 |
| Stiffness to Weight: Bending, points | 43 | |
| 34 to 39 |
| Strength to Weight: Axial, points | 5.6 | |
| 11 to 15 |
| Strength to Weight: Bending, points | 14 | |
| 25 to 30 |
| Thermal Diffusivity, mm2/s | 0.28 | |
| 0.13 |