Monel K-500 vs. N07041 Nickel
Both Monel K-500 and N07041 nickel are nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is Monel K-500 and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 220 |
| Elongation at Break, % | 25 to 36 | |
| 14 |
| Fatigue Strength, MPa | 260 to 560 | |
| 540 |
| Shear Strength, MPa | 430 to 700 | |
| 850 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 1100 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 310 to 880 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1320 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 450 |
| Thermal Conductivity, W/m-K | 18 | |
| 11 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.7 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 to 260 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 2420 | |
| 2510 |
| Stiffness to Weight: Axial, points | 10 | |
| 15 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 35 | |
| 47 |
| Strength to Weight: Bending, points | 19 to 27 | |
| 34 |
| Thermal Diffusivity, mm2/s | 4.8 | |
| 3.0 |
| Thermal Shock Resistance, points | 21 to 36 | |
| 38 |