Monel K-500 vs. R05240 Alloy
Monel K-500 belongs to the nickel alloys classification, while R05240 alloy belongs to the otherwise unclassified metals. There are 18 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is Monel K-500 and the bottom bar is R05240 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 160 | |
150 |
Elongation at Break, % | 25 to 36 | |
25 |
Poisson's Ratio | 0.32 | |
0.36 |
Shear Modulus, GPa | 61 | |
57 |
Tensile Strength: Ultimate (UTS), MPa | 640 to 1100 | |
270 |
Tensile Strength: Yield (Proof), MPa | 310 to 880 | |
170 |
Thermal Properties
Latent Heat of Fusion, J/g | 270 | |
210 |
Specific Heat Capacity, J/kg-K | 440 | |
190 |
Thermal Expansion, µm/m-K | 14 | |
6.8 |
Otherwise Unclassified Properties
Density, g/cm3 | 8.7 | |
14 |
Embodied Water, L/kg | 280 | |
460 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 180 to 260 | |
59 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 300 to 2420 | |
90 |
Stiffness to Weight: Axial, points | 10 | |
6.3 |
Stiffness to Weight: Bending, points | 21 | |
13 |
Strength to Weight: Axial, points | 21 to 35 | |
5.4 |
Strength to Weight: Bending, points | 19 to 27 | |
6.8 |
Thermal Shock Resistance, points | 21 to 36 | |
18 |
Alloy Composition
Aluminum (Al), % | 2.3 to 3.2 | |
0 |
Carbon (C), % | 0 to 0.18 | |
0 to 0.010 |
Copper (Cu), % | 27 to 33 | |
0 |
Hydrogen (H), % | 0 | |
0 to 0.0015 |
Iron (Fe), % | 0 to 2.0 | |
0 to 0.010 |
Manganese (Mn), % | 0 to 1.5 | |
0 |
Molybdenum (Mo), % | 0 | |
0 to 0.020 |
Nickel (Ni), % | 63 to 70.4 | |
0 to 0.010 |
Niobium (Nb), % | 0 | |
35 to 42 |
Nitrogen (N), % | 0 | |
0 to 0.010 |
Oxygen (O), % | 0 | |
0 to 0.020 |
Silicon (Si), % | 0 to 0.5 | |
0 to 0.0050 |
Sulfur (S), % | 0 to 0.010 | |
0 |
Tantalum (Ta), % | 0 | |
57.9 to 65 |
Titanium (Ti), % | 0.35 to 0.85 | |
0 to 0.010 |
Tungsten (W), % | 0 | |
0 to 0.050 |