Mullite vs. Carbon-carbon
Mullite belongs to the oxide-based engineering ceramics classification, while carbon-carbon belongs to the non-oxide engineering ceramics. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is mullite and the bottom bar is carbon-carbon.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 800 | |
| 240 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 to 170 | |
| 95 |
| Poisson's Ratio | 0.25 | |
| 0.32 |
| Tensile Strength: Ultimate (UTS), MPa | 160 | |
| 19 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1680 | |
| 2400 |
| Specific Heat Capacity, J/kg-K | 950 | |
| 760 |
| Thermal Conductivity, W/m-K | 3.5 to 11 | |
| 40 |
| Thermal Expansion, µm/m-K | 5.8 | |
| 4.0 |
Electrical Properties
| Electrical Resistivity Order of Magnitude, 10x Ω-m | 10 to 11 | |
| -5.0 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 to 3.0 | |
| 1.7 |
Common Calculations
| Stiffness to Weight: Axial, points | 22 to 31 | |
| 31 |
| Stiffness to Weight: Bending, points | 58 to 62 | |
| 89 |
| Strength to Weight: Axial, points | 15 to 17 | |
| 3.0 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 9.1 |
| Thermal Diffusivity, mm2/s | 1.4 to 3.7 | |
| 31 |
| Thermal Shock Resistance, points | 12 to 19 | |
| 3.5 |