Mullite vs. Granite
Mullite belongs to the oxide-based engineering ceramics classification, while granite belongs to the natural stone. There are 17 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is mullite and the bottom bar is granite.
Metric UnitsUS Customary Units
Mechanical Properties
| Compressive (Crushing) Strength, MPa | 800 | |
| 2200 |
| Elastic (Young's, Tensile) Modulus, GPa | 110 to 170 | |
| 70 |
| Flexural Strength, MPa | 130 to 160 | |
| 24 |
| Poisson's Ratio | 0.25 | |
| 0.25 |
| Tensile Strength: Ultimate (UTS), MPa | 160 | |
| 39 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 1680 | |
| 350 |
| Specific Heat Capacity, J/kg-K | 950 | |
| 840 |
| Thermal Conductivity, W/m-K | 3.5 to 11 | |
| 2.7 |
| Thermal Expansion, µm/m-K | 5.8 | |
| 7.4 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 16 to 17 | |
| 8.5 |
Otherwise Unclassified Properties
| Density, g/cm3 | 2.7 to 3.0 | |
| 2.9 |
Common Calculations
| Stiffness to Weight: Axial, points | 22 to 31 | |
| 14 |
| Stiffness to Weight: Bending, points | 58 to 62 | |
| 48 |
| Strength to Weight: Axial, points | 15 to 17 | |
| 3.8 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 9.0 |
| Thermal Diffusivity, mm2/s | 1.4 to 3.7 | |
| 1.1 |
| Thermal Shock Resistance, points | 12 to 19 | |
| 5.4 |