NEMA Laminate vs. PVDF
NEMA laminate belongs to the thermoset plastics classification, while PVDF belongs to the thermoplastics. There are 11 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is NEMA laminate and the bottom bar is PVDF.
Metric UnitsUS Customary Units
Mechanical Properties
| Flexural Modulus, GPa | 6.4 to 18 | |
| 1.5 |
| Flexural Strength, MPa | 87 to 340 | |
| 75 |
| Impact Strength: Notched Izod, J/m | 20 to 430 | |
| 180 |
| Tensile Strength: Ultimate (UTS), MPa | 55 to 260 | |
| 49 |
Thermal Properties
| Maximum Temperature: Mechanical, °C | 120 to 200 | |
| 140 |
| Thermal Expansion, µm/m-K | 9.0 to 20 | |
| 120 |
Electrical Properties
| Dielectric Strength (Breakdown Potential), kV/mm | 12 to 21 | |
| 10 |
Otherwise Unclassified Properties
| Density, g/cm3 | 1.3 to 1.9 | |
| 1.8 |
| Water Absorption After 24 Hours, % | 0.17 to 3.5 | |
| 0 |
Common Calculations
| Strength to Weight: Axial, points | 8.3 to 40 | |
| 7.8 |
| Strength to Weight: Bending, points | 17 to 50 | |
| 17 |