Nickel 200 vs. ACI-ASTM CG6MMN Steel
Nickel 200 belongs to the nickel alloys classification, while ACI-ASTM CG6MMN steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is nickel 200 and the bottom bar is ACI-ASTM CG6MMN steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 200 |
| Elongation at Break, % | 23 to 44 | |
| 34 |
| Fatigue Strength, MPa | 120 to 350 | |
| 260 |
| Poisson's Ratio | 0.31 | |
| 0.28 |
| Shear Modulus, GPa | 70 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 420 to 540 | |
| 670 |
| Tensile Strength: Yield (Proof), MPa | 120 to 370 | |
| 320 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 1080 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1420 |
| Melting Onset (Solidus), °C | 1440 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 22 |
| Density, g/cm3 | 8.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 4.8 |
| Embodied Energy, MJ/kg | 150 | |
| 68 |
| Embodied Water, L/kg | 230 | |
| 180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 150 | |
| 190 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 42 to 370 | |
| 260 |
| Stiffness to Weight: Axial, points | 11 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 25 |
| Strength to Weight: Axial, points | 13 to 17 | |
| 24 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 22 |
| Thermal Shock Resistance, points | 13 to 16 | |
| 14 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.060 |
| Chromium (Cr), % | 0 | |
| 20.5 to 23.5 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 51.9 to 62.1 |
| Manganese (Mn), % | 0 to 0.35 | |
| 4.0 to 6.0 |
| Molybdenum (Mo), % | 0 | |
| 1.5 to 3.0 |
| Nickel (Ni), % | 99 to 100 | |
| 11.5 to 13.5 |
| Niobium (Nb), % | 0 | |
| 0.1 to 0.3 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.4 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.3 |