Nickel 200 vs. EN 1.0214 Steel
Nickel 200 belongs to the nickel alloys classification, while EN 1.0214 steel belongs to the iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is nickel 200 and the bottom bar is EN 1.0214 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 190 |
| Elongation at Break, % | 23 to 44 | |
| 12 to 31 |
| Fatigue Strength, MPa | 120 to 350 | |
| 160 to 250 |
| Poisson's Ratio | 0.31 | |
| 0.29 |
| Shear Modulus, GPa | 70 | |
| 73 |
| Shear Strength, MPa | 300 to 340 | |
| 250 to 290 |
| Tensile Strength: Ultimate (UTS), MPa | 420 to 540 | |
| 330 to 460 |
| Tensile Strength: Yield (Proof), MPa | 120 to 370 | |
| 210 to 360 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1470 |
| Melting Onset (Solidus), °C | 1440 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 470 |
| Thermal Conductivity, W/m-K | 69 | |
| 53 |
| Thermal Expansion, µm/m-K | 13 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 18 | |
| 6.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 18 | |
| 7.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 1.8 |
| Density, g/cm3 | 8.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 1.4 |
| Embodied Energy, MJ/kg | 150 | |
| 18 |
| Embodied Water, L/kg | 230 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 150 | |
| 34 to 130 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 42 to 370 | |
| 120 to 340 |
| Stiffness to Weight: Axial, points | 11 | |
| 13 |
| Stiffness to Weight: Bending, points | 21 | |
| 24 |
| Strength to Weight: Axial, points | 13 to 17 | |
| 12 to 16 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 14 to 17 |
| Thermal Diffusivity, mm2/s | 17 | |
| 14 |
| Thermal Shock Resistance, points | 13 to 16 | |
| 11 to 14 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.020 to 0.060 |
| Carbon (C), % | 0 to 0.15 | |
| 0.080 to 0.12 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 0 to 0.4 | |
| 99.17 to 99.6 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.3 to 0.5 |
| Nickel (Ni), % | 99 to 100 | |
| 0 |
| Phosphorus (P), % | 0 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.025 |