Nickel 201 vs. 6023 Aluminum
Nickel 201 belongs to the nickel alloys classification, while 6023 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is nickel 201 and the bottom bar is 6023 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 180 | |
| 69 |
| Elongation at Break, % | 4.5 to 45 | |
| 11 |
| Fatigue Strength, MPa | 42 to 210 | |
| 120 to 130 |
| Poisson's Ratio | 0.31 | |
| 0.33 |
| Shear Modulus, GPa | 70 | |
| 26 |
| Shear Strength, MPa | 270 to 380 | |
| 210 to 220 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 660 | |
| 360 |
| Tensile Strength: Yield (Proof), MPa | 80 to 510 | |
| 300 to 310 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 400 |
| Maximum Temperature: Mechanical, °C | 900 | |
| 160 |
| Melting Completion (Liquidus), °C | 1450 | |
| 640 |
| Melting Onset (Solidus), °C | 1440 | |
| 580 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 890 |
| Thermal Conductivity, W/m-K | 78 | |
| 170 |
| Thermal Expansion, µm/m-K | 13 | |
| 23 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 19 | |
| 45 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 140 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 65 | |
| 11 |
| Density, g/cm3 | 8.9 | |
| 2.8 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 8.3 |
| Embodied Energy, MJ/kg | 150 | |
| 150 |
| Embodied Water, L/kg | 230 | |
| 1180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 25 to 130 | |
| 38 to 39 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 17 to 720 | |
| 670 to 690 |
| Stiffness to Weight: Axial, points | 11 | |
| 14 |
| Stiffness to Weight: Bending, points | 21 | |
| 49 |
| Strength to Weight: Axial, points | 12 to 20 | |
| 35 to 36 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 40 |
| Thermal Diffusivity, mm2/s | 20 | |
| 67 |
| Thermal Shock Resistance, points | 11 to 19 | |
| 16 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 94 to 97.7 |
| Bismuth (Bi), % | 0 | |
| 0.3 to 0.8 |
| Carbon (C), % | 0 to 0.020 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 0.2 to 0.5 |
| Iron (Fe), % | 0 to 0.4 | |
| 0 to 0.5 |
| Magnesium (Mg), % | 0 | |
| 0.4 to 0.9 |
| Manganese (Mn), % | 0 to 0.35 | |
| 0.2 to 0.6 |
| Nickel (Ni), % | 99 to 100 | |
| 0 |
| Silicon (Si), % | 0 to 0.35 | |
| 0.6 to 1.4 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0.6 to 1.2 |
| Residuals, % | 0 | |
| 0 to 0.15 |