Nickel 201 vs. 90-silver 10-cadmium-oxide
Nickel 201 belongs to the nickel alloys classification, while 90-silver 10-cadmium-oxide belongs to the otherwise unclassified metals. There are 8 material properties with values for both materials. Properties with values for just one material (23, in this case) are not shown.
For each property being compared, the top bar is nickel 201 and the bottom bar is 90-silver 10-cadmium-oxide.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 8.9 | |
| 10 |
| Electrical Conductivity: Equal Volume, % IACS | 19 | |
| 72 to 100 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 19 | |
| 64 to 91 |
| Elongation at Break, % | 4.5 to 45 | |
| 1.1 to 28 |
| Shear Strength, MPa | 270 to 380 | |
| 170 to 230 |
| Strength to Weight: Axial, points | 12 to 20 | |
| 7.0 to 11 |
| Strength to Weight: Bending, points | 13 to 19 | |
| 8.8 to 12 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 660 | |
| 260 to 400 |