Nickel 201 vs. N08120 Nickel

Both nickel 201 and N08120 nickel are nickel alloys. They have a modest 38% of their average alloy composition in common, which, by itself, doesn't mean much. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is nickel 201 and the bottom bar is N08120 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 180
200
Elongation at Break, % 4.5 to 45
34
Fatigue Strength, MPa 42 to 210
230
Poisson's Ratio 0.31
0.28
Shear Modulus, GPa 70
79
Shear Strength, MPa 270 to 380
470
Tensile Strength: Ultimate (UTS), MPa 390 to 660
700
Tensile Strength: Yield (Proof), MPa 80 to 510
310

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Maximum Temperature: Mechanical, °C 900
1000
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1440
1370
Specific Heat Capacity, J/kg-K 440
470
Thermal Conductivity, W/m-K 78
11
Thermal Expansion, µm/m-K 13
14

Otherwise Unclassified Properties

Base Metal Price, % relative 65
45
Density, g/cm3 8.9
8.2
Embodied Carbon, kg CO2/kg material 11
7.2
Embodied Energy, MJ/kg 150
100
Embodied Water, L/kg 230
240

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 25 to 130
190
Resilience: Unit (Modulus of Resilience), kJ/m3 17 to 720
240
Stiffness to Weight: Axial, points 11
14
Stiffness to Weight: Bending, points 21
24
Strength to Weight: Axial, points 12 to 20
24
Strength to Weight: Bending, points 13 to 19
21
Thermal Diffusivity, mm2/s 20
3.0
Thermal Shock Resistance, points 11 to 19
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Boron (B), % 0
0 to 0.010
Carbon (C), % 0 to 0.020
0.020 to 0.1
Chromium (Cr), % 0
23 to 27
Cobalt (Co), % 0
0 to 3.0
Copper (Cu), % 0 to 0.25
0 to 0.5
Iron (Fe), % 0 to 0.4
21 to 41.4
Manganese (Mn), % 0 to 0.35
0 to 1.5
Molybdenum (Mo), % 0
0 to 2.5
Nickel (Ni), % 99 to 100
35 to 39
Niobium (Nb), % 0
0.4 to 0.9
Nitrogen (N), % 0
0.15 to 0.3
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0
0 to 0.2
Tungsten (W), % 0
0 to 2.5